Ni influence, on growth of chemically deposited PbS films

H Lima Lima, C Aguilar Galicia

Resumen


Abstract:

PbS films growth by chemical bath is presented. The morphological changes of the PbS were analyzed using the Scanning Electron microscopy. The grain size determined by x-Ray Diffraction of the undoped samples, was found ~36 nm and the doped ~32-5 nm.
Keywords: Thin films, nanocrystalline, quantum effect, Gibbs free energy, coordination complex.


Resumen:

Películas de PbS crecidas por Baño Químico es presentada. Los cambios morfológicos fueron analizados utilizando Microscopia Electrónica de Barrido. El tamaño de grano es determinado por Difracción de Rayos X en las muestras no dopadas, es de ~36 nm y las dopadas ~32-5 nm.
Palabras clave: Películas delgadas, nanocristales, efecto cuántico, energía libre de Gibbs, complejo de coordinación.


Referencias


A. J. Bethune, (1969).N.A.S Loud. in

Standard Aqueous Potential a Temperature

Coefficients at 25 °C, C. C. Hampel, Skokie,

II.

Brus L. E.(1984), Electron-electron and

Electron-Hole Interactions in Small

Semiconductor Crystallites: The Size

Dependence of the Lowest Excited Electronic

State, J. Chem. Phys. 80: 4403-4409.

Davin Yu, Wang, Zhaoyu Meng, Jun Lu and

Yitai Quian.(2002). Synthesis of closed PbS

nanowires with regular geometric

morphologies, J. Mater. Chem. 12:403-405.

O. Zelaya Ángel, S. A. Tomas, P. Rodríguez,

J. G. Mendoza Álvarez, R. Lozada Morales,

O. Portillo Moreno, J. González

Hernández(2011).Enhancement of

photoluminescence due to erbium-doped in

CdS thin films, J. Mater Sci. 1: 1-7.

O. Portillo Moreno, H. Lima Lima, V.

Ramírez Falcón, J. Martínez Juárez, G.

Juárez. Díaz, R. Lozada Morales, R. Rebollo

Plata, R. Palomino Merino, A. B. Soto

Guzmán, O. Zelaya Ángel(2006).Growth of

CdS:Cu Nanocrystals by Chemical Synthesis,

J. Electrochem. Soc.,153: 926-930.

O. Portillo Moreno, H. Lima Lima, R. Lozada Morales, R. Palomino Merino, O. Zelaya Ángel(2005). J. Mat. Sci. 40:4489-4492.

O. Portillo Moreno, M. Chávez Portillo, M. Moreno Flores, J. Martínez Juárez, G. Abarca Ávila, R. Lozada Morales O. Zelaya Ángel (2011). Properties of Chemical Bath Deposited PbS Thin Films Doped with Cd2+ Journal of Materials Science and Engineering A 1: 759-767.

Pingtang Zhao, Jinmin Wang, Guoe Cheng, and Kaixun Huang (2010).Fabrication of Symmetric Hierarchical Hollow PbS Microcrystals via a Facile Solvothermal Process, J. Phys. Chem. B 110: 22400-22406.

P. K. Nair, O. Gomezdaza, M. T. S. Nair(1992). Metal sulfide thin film photography with lead sulfide thin films, Adv. Mater, Opt. Electron, 1:139-145.

R. Reisfeld, C. K. Jorgensen (1996).Structure and Bonding, vol. 85, Springer, Berlin, p. 99.

Rakesh K. Joshi, Aloke Kanjilal, H. K. Shegal.(2004).Solution grown PbS nanoparticles films, Appl. Surf. Sci.221: 43-47.

S. B. Pawar, J. S. Shaikh, R. S. Devan, Y. R. Ma. D. Haranath, P. N. Bhosale, P. S. Patil(2011). Facile and low cost chemosynthesis of nanostructured PbS with tunable optical properties, Applied SurfaceScience 258: 1869-1875.

Sang-Min Lee, Young-Wook Jun, Sung-Nam Cho, and Jinwoo Cheon, Single crystalline Star-Shaped nanocrystals and their Evolution: programming the geometry of Nanobuilding Bloks, J. Am. Chem. Soc. 124:11244-11245.

Shenglin Xiong, Baojuan Xi, Dechen Xu, Chengming Wang, Xiaoming Feng, Hongyang Zhou, and Yitai Quian(2007). L-Cysteine-Assisted Tunable Synthesis of PbS of Various Morphologies, J. Phys. Chem. 111: 16761-16767.

T. Saraidarov, R. Reisfeld, A. Sashchiuk, E. Lifshitz(2007). Synthesis and characterization of PbS nanorods and nanowires, Physica E 37: 173-177.

Thangavel, S. Ganesan, K. Saravanan (2012).Annealing effect on cadmium in situ doping of chemical bath deposited PbS thin films, Thin Solid Films.520:5206-5210.

E. Pentia, L. Pintillie(2001). T. Botila, A. Chaparro (2003). Bi influence on growth physical properties of chemical deposited PbS films, Thin Solid Films, 434:162-170.

ZepingPeng, Yusheng Jiang, Yonghai Song, Cheng Wang, and Hongjie Zhang(2008). Morphology Control of nanoscala PbS Particles in Polyol Process, Chem. Mater. 20: 3153-3162


Enlaces refback

  • No hay ningún enlace refback.


Naturaleza y Tecnología, revista electrónica de la División de Ciencias Naturales y Exactas del campus Guanajuato, Universidad de Guanajuato. En ella se reciben para su revisión y arbitraje, artículos originales de investigación, artículos de revisión sobre temas actuales de investigación, así como ensayos sobre diversas temáticas del mundo científico y académico en las áreas de la química, matemáticas, ingeniería, astronomía, biología y farmacia, dentro del ámbito que comprenden las ciencias naturales y exactas, siendo requerido que no hayan sido publicadas o en proceso de publicación en otras revistas. Cuenta también con un Facebook de notas científicas de actualidad como apoyo a la actividad académica de la comunidad universitaria y para conocimiento del público en general como parte de un programa de divulgación científica y tecnológica.

.